64 anodized titanium plate Technology

Previously used for the experiments.
The aqueous solution was distilled with sulfuric acid, the sulfuric acid concentration is low , less than 1:10.
Begin to make experiments with waste titanium , titanium anode , cathode with a thick copper wire when , put together the above electrolyte. Through the power after the bubble began to take . As shown below:

64 titanium grip put down after treatment to determine OK. Voltage of 15V, the transformer is Xiao Xu sent me medical titanium plates , the highest is 15V. Note that a look at the newspapers there is a pattern of untreated titanium , polished surface first , polished .

Aqueous solution of copper sulfate solution slowly turns blue .

At first I did not know how long you want energized , so to say , " as long as possible ," the right piece over 10 minutes ,
The results far from ideal, the left made ​​a piece about 1 minute. Then I put it in addition to redo grind , grind fine addition to the oxide layer . Re- energized, about a half a minute electricity , pretty much .

I think , to deal with the surface of titanium must be careful before grinding , I used 800 sandpaper , good surface is very smooth. There I found the process to make electricity anodized , you can look at the situation first processing power , and then decide whether or not to continue energized.
Then I will try other colors of the oxide layer , but to buy DCPOWERSUPPLY high pressure points ,titanium axle  at least 50V.

Interesting chemistry experiment , anode cathode copper melting went to go .

Some people say , titanium anodizing can be performed in any conductive liquid , such as : Coca-Cola , Sprite , orange juice, watermelon juice , water , etc., can choose their own experiments .